The ability of the synthesized magnetic particles to eliminate the heavy metal ions under investigation was contrasted with other adsorbents reported in the literature, as listed in Table 6. The adsorbent employed in this study showed better adsorption performance than others, indicating that the tested nanopowder is a good candidate for cadmium and nickel ions removal from aqueous solutions.

Table 6

A comparison of (x)ZnO(1 − x)Fe2O3 adsorption capacity with other adsorbents for cadmium and nickel metal ions

AdsorbentNi(II) (mg·g−1)Cd(II) (mg·g−1)Temp. (K)Reference
Silica-gel-biomass 98.01 – 298 Akar et al. (2009)  
CuFe2O4 nano-particles – 17.54 298 Tu et al. (2012)  
NH2-MCM-41 12.36 18.25 298 Heidari et al. (2009)  
Magnetic graphene oxide – 91.29 298 Deng et al. (2013)  
Milled goethite – 125 298 Khezami et al. (2016)  
Milled goethite – 167 328 Khezami et al. (2016)  
Ni (15% wt)-doped α-Fe2O3 – 90.91 328 OuldM'hamed et al. (2015)  
Magnetic nanoparticles 11.53 – 298 Sharma & Srivastava (2010)  
Lemon peel 80.0 – 298 Thirumavalavan et al. (2011)  
Orange peel 81.3 – 298 Thirumavalavan et al. (2011)  
ZnFe2O4 57.1 104.2 298 Present work 
ZnFe2O4 83 128 328 Present work 
AdsorbentNi(II) (mg·g−1)Cd(II) (mg·g−1)Temp. (K)Reference
Silica-gel-biomass 98.01 – 298 Akar et al. (2009)  
CuFe2O4 nano-particles – 17.54 298 Tu et al. (2012)  
NH2-MCM-41 12.36 18.25 298 Heidari et al. (2009)  
Magnetic graphene oxide – 91.29 298 Deng et al. (2013)  
Milled goethite – 125 298 Khezami et al. (2016)  
Milled goethite – 167 328 Khezami et al. (2016)  
Ni (15% wt)-doped α-Fe2O3 – 90.91 328 OuldM'hamed et al. (2015)  
Magnetic nanoparticles 11.53 – 298 Sharma & Srivastava (2010)  
Lemon peel 80.0 – 298 Thirumavalavan et al. (2011)  
Orange peel 81.3 – 298 Thirumavalavan et al. (2011)  
ZnFe2O4 57.1 104.2 298 Present work 
ZnFe2O4 83 128 328 Present work 