The MMT, SD and PH were pulverized to powder form. The binary composites were composed of MMT and SD weighed in different ratios as shown in Table 1. The ternary composites were composed of MMT, SD and PH weighed in different ratios as shown in Table 1.

Table 1

Molar ratios by mass of MMT: SD: PH

Ternary composite
Binary composite
Sample IDMMT/gSD/gPH/gSample I.DMMT/gSD/g
S1 9.0 0.5 0.5 M1 9.0 1.0 
S2 8.0 1.0 1.0 M2 8.0 2.0 
S3 7.0 1.5 1.5 M3 7.0 3.0 
S4 6.0 2.0 2.0 M4 6.0 4.0 
S5 5.0 2.5 2.5 M5 5.0 5.0 
S6 4.0 3.0 3.0 M6 4.0 6.0 
S7 3.0 3.5 3.5 M7 3.0 7.0 
S8 2.0 4.0 4.0 M8 2.0 8.0 
S9 1.0 4.5 4.5 M9 1.0 9.0 
Ternary composite
Binary composite
Sample IDMMT/gSD/gPH/gSample I.DMMT/gSD/g
S1 9.0 0.5 0.5 M1 9.0 1.0 
S2 8.0 1.0 1.0 M2 8.0 2.0 
S3 7.0 1.5 1.5 M3 7.0 3.0 
S4 6.0 2.0 2.0 M4 6.0 4.0 
S5 5.0 2.5 2.5 M5 5.0 5.0 
S6 4.0 3.0 3.0 M6 4.0 6.0 
S7 3.0 3.5 3.5 M7 3.0 7.0 
S8 2.0 4.0 4.0 M8 2.0 8.0 
S9 1.0 4.5 4.5 M9 1.0 9.0 

Close Modal

or Create an Account

Close Modal
Close Modal