Table 4

Fitting parameters of deconvoluted Bi 4f XPS spectra for Ti1-xBixO2 (x = 0.01, x = 0.03, x = 0.05, x = 0.10) samples

SampleBi 4f7/2
ΔE1Bi 4f5/2
ΔE2
Bi 4f7/2(1)
Bi 4f7/2(2)
Bi 4f5/2(1)
Bi 4f5/2(2)
B.ExFWyAzB.ExFWyAzB.ExFWyAzB.ExFWyAz
x= 0.01 159.19 1.36 176.107 158.24 1.91 60.914 0.95 166.50 1.45 164.954 164.62 1.81 35.0319 1.88 
x= 0.03 160.00 3.79 1,115.16 158.35 1.57 641.652 1.65 166.54 2.76 584.831 164.79 1.73 511.807 1.75 
x= 0.05 159.21 1.62 1,999.34 158.20 1.72 71.3654 1.01 166.62 1.58 1,271.75 164.09 1.35 232.819 2.53 
x= 0.10 159.18 1.49 1,022.83 158.48 1.74 99.6585 0.7 166.47 1.53 810.443 164.53 1.43 57.468 1.94 
SampleBi 4f7/2
ΔE1Bi 4f5/2
ΔE2
Bi 4f7/2(1)
Bi 4f7/2(2)
Bi 4f5/2(1)
Bi 4f5/2(2)
B.ExFWyAzB.ExFWyAzB.ExFWyAzB.ExFWyAz
x= 0.01 159.19 1.36 176.107 158.24 1.91 60.914 0.95 166.50 1.45 164.954 164.62 1.81 35.0319 1.88 
x= 0.03 160.00 3.79 1,115.16 158.35 1.57 641.652 1.65 166.54 2.76 584.831 164.79 1.73 511.807 1.75 
x= 0.05 159.21 1.62 1,999.34 158.20 1.72 71.3654 1.01 166.62 1.58 1,271.75 164.09 1.35 232.819 2.53 
x= 0.10 159.18 1.49 1,022.83 158.48 1.74 99.6585 0.7 166.47 1.53 810.443 164.53 1.43 57.468 1.94 

xBinding energies, yfull width at half maximum, zcorresponding area of the peaks, and ΔE1 is the binding energy between Bi 4f7/2(1) and Bi 4f7/2(2) whereas ΔE2 is the binding energy between Bi 4f5/2(1) and Bi 4f5/2(2).