Nanofibers for bacterial elimination

PolymerMembrane thickness (nm)CharacteristicsAntibacterial action
Polyacrylonitrile 100 Average hole dimension: 0.22 ± 0.01 μm, Flux: 1.5 L/m2E. coli 
Polyacrylonitrile 50 Average hole dimension: 0.4 μm S. aureus, E. coli 
Nylon − 6 650 OD culture at 600 nm 
E. coli pristine − 3.4, Mat 1 − 1.57, Mat 2 − 1.75 S. aureus 
S. aureus pristine − 2055, Mat 1 − 1.68, Mat 2 − 1.88 E. coli 
Polyacrylonitrile (PAN) 200 Area reticence (mm) 
Microorganism NaBh4 reduction Heated @160 °C Heated @80 °C  
B. subtlilis 7.5 10 B. subtlilis 
S. aureus 10 10 S. aureus 
E. coli – E. coli 
PolymerMembrane thickness (nm)CharacteristicsAntibacterial action
Polyacrylonitrile 100 Average hole dimension: 0.22 ± 0.01 μm, Flux: 1.5 L/m2E. coli 
Polyacrylonitrile 50 Average hole dimension: 0.4 μm S. aureus, E. coli 
Nylon − 6 650 OD culture at 600 nm 
E. coli pristine − 3.4, Mat 1 − 1.57, Mat 2 − 1.75 S. aureus 
S. aureus pristine − 2055, Mat 1 − 1.68, Mat 2 − 1.88 E. coli 
Polyacrylonitrile (PAN) 200 Area reticence (mm) 
Microorganism NaBh4 reduction Heated @160 °C Heated @80 °C  
B. subtlilis 7.5 10 B. subtlilis 
S. aureus 10 10 S. aureus 
E. coli – E. coli 