This study was undertaken to examine the degradation of TNT, RDX and HMX in a circular photocatalytic reactor with TiO2 as a photocatalyst. We examined the impact of parameters such as the initial concentration, initial pH of solution on rates of photocatalized transformation, and the mineralization. The results showed that photocatalysis is an effective process for the degradation of TNT, RDX and HMX. They could be completely degraded in 150 min with 1.0 g/L TiO2 at pH 7. An increase in the photocatalytic degradation of HMX was noticed with decreasing initial HMX. The rates of RDX and HMX degradation were greater in neutral pH than in acidic and alkaline conditions. In case of TNT degradation, the rate of degradation was the fastest at pH 11. Approximately 82% TOC decrease in the TNT degradation was achieved after 150 min, whereas TOC decrease in RDX and HMX was 24% and 59%, respectively. Nitrate, nitrite, and ammonium ions were detected as the nitrogen byproducts from the photocatalysis, and more than 50% of the total nitrogen was recovered as nitrate ion in every explosives.
Skip Nav Destination
Research Article| December 01 2002
Photocatalytic degradation of explosives contaminated water
Water Sci Technol (2002) 46 (11-12): 139–145.
S.-J. Lee, H.-S. Son, H.-K. Lee, K.-D. Zoh; Photocatalytic degradation of explosives contaminated water. Water Sci Technol 1 December 2002; 46 (11-12): 139–145. doi: https://doi.org/10.2166/wst.2002.0729
Download citation file: