At different calcination conditions, titanium-based manganese oxides (MnOx) electrodes were fabricated by spraying method without adhesive. The MnOx/Ti electrodes were applied in electrochemical oxidation of wastewater treatment for the first time. The surface morphologies of electrodes were tested by scanning electron microscopy. The formation of different manganese oxidation states on electrodes was confirmed by X-ray diffraction and X-ray photoelectron spectroscopy. The electrochemical properties of the electrodes have been performed by means of cyclic voltammetry and electrochemical impedance spectroscopy. The characterizations revealed that the MnOx/Ti-350(20) electrode, prepared at calcination temperature of 350 °C for 20 min, exhibited fewer cracks on the electrode surface, larger electrochemically effective surface area and lower charge transfer resistance than electrodes prepared at other calcination conditions. Moreover, Acid Red B was used as target pollutant to test the electrode activity via monitoring the concentration changes by UV spectrophotometer. The results showed that the MnOx/Ti-350(20) electrode presented the best performance on decolorization of Acid Red B with the lowest cell potential during the process of electrochemical oxidation, and the chemical oxygen demand (COD) conversion was 50.7%. Furthermore, the changes of Acid Red B during the electrochemical oxidation process were proposed by the UV–vis spectra.

You do not currently have access to this content.