The exhausted activated carbon generated from the adsorption of heavy metal wastewater needs further treatment/disposal. In this study, a new application of copper-spent activated carbon (Cu-AC) was proposed. Cu-AC was used to activate peroxydisulfate (PDS) for the decolorization of Acid Orange 7 (AO7) and electrical current was introduced to enhance the process. The decolorization followed a pseudo-first-order kinetic pattern well (R2 > 0.95). 92.4% of color removal at 60 min and 38.3% of total organic carbon removal at 180 min were achieved when initial pH value was 9.0, current density was 16 mA/cm2, PDS concentration was 5 mM and Cu-AC dosage was 0.25 g/L. The radical scavengers including methanol, tert-butanol and phenol, as well as electron paramagnetic resonance test, were employed to investigate the oxidizing species responsible for AO7 decolorization. The stability of Cu-AC was confirmed by three recycle experiments.
The dye wastewater is considered as bio-refractory and can hardly be degraded by conventional wastewater treatment processes (Yang et al. 2011). The activated persulfate process has been proved to degrade azo dyes effectively using highly reactive species such as sulfate radicals (Zhou et al. 2015). Among various activation methods, homogeneous activated persulfate using transition metals has attracted great attention (Lei et al. 2015b). However, the transition metal activated process is only effective under acid conditions and high metal sludge is generated during the neutralization stage before the effluent is discharged (Wu et al. 2012). To overcome these drawbacks, heterogeneous metal catalysts were synthesized to activate persulfate under a wide pH range (Cai et al. 2015b). Activated carbon (AC) is considered as a good catalyst support and AC supported metal catalysts have been used to activate persulfate (Cai et al. 2014a, 2015a).
As a good adsorbent, AC has also been widely applied to the adsorptive removal of heavy metal from wastewater (Demirbas et al. 2009). Nevertheless, heavy metal exhausted AC will cause secondary pollution and needs further treatment/disposal. In this study, a new application of copper-spent activated carbon (Cu-AC) was proposed in which Cu-AC was employed as a catalyst to activate persulfate and electrical current was introduced to enhance the heterogeneous activation process (Cai et al. 2014b; Lin et al. 2014b). The activity and stability of Cu-AC was evaluated, the reactive radicals generated in this process were identified, and the effect of important parameters on color removal was investigated.
METHODS AND MATERIALS
Acid Orange 7 (AO7, C16H11N2NaO4S) with reagent purity grade was obtained from Sinopharm Chemical Reagent Co., Ltd (China). AC was purchased from Aladdin Industrial Corporation (Shanghai, China). Before utilization, AC was washed with abundant deionized water to wash off the impurity on the surface and subsequently dried at 120 °C for 24 h before being sealed in hermetic bags.
Copper adsorption experiments were conducted in a series of 500 mL beakers. At the designated time, 5 mL solutions were taken to determine the residual copper concentration. After 24 h adsorption, the saturated AC (Cu-AC) was filtered and dried at 120 °C for 24 h.
The experimental set up of decolorization was similar to our previous study (Lin et al. 2013b). In each run, a fresh stock solution of AO7 was prepared in deionized water with the initial concentration (C0) of 100 mg/L. The initial pH (pH0) was adjusted by 1 mol/L sulfuric acid or 1 mol/L sodium hydroxide after peroxydisulfate (PDS) and supporting electrolyte Na2SO4 (50 mM) were applied. The decolorization of AO7 was conducted in a 250 mL glass beaker at constant current using a plate anode (Ti/RuO2–IrO2) and a plate cathode (stainless steel). Both anode and cathode have the same dimensions (5.0 × 11.9 cm) and the electrode gap is 4.0 cm. A magnetic stirrer with a water bath was used to mix the solution and to keep the temperature at 25 °C. The reaction was initiated when the direct current power was turned on and the Cu-AC was added. At pre-selected time intervals, 2 mL aliquot was withdrawn and filtered through 0.45 μm membranes before analysis.
The absorbency of AO7 was monitored at λ = 485 nm using a Rayleigh UV-9100 spectrophotometer (China). The concentration of residual PDS was measured by iodometric titration with thiosulfate. The concentration of copper ion was determined by atomic absorption spectrometer. Total organic carbon (TOC) was measured by a Jena multi N/C 3100 TOC analyzer. The reactive radicals were examined with 5,5-dimethyl-1-pytroline N-oxide (DMPO) as a spin-trapping agent by electron paramagnetic resonance (EPR) using a JEOL FA 200 spectrometer.
RESULTS AND DISCUSSION
AO7 decolorization under different systems
Therefore, the highest color removal (95.7%) was achieved in the EC/PDS/Cu-AC system.
The results of kinetic analysis indicated that the decolorization of AO7 followed a pseudo-first-order model with correlation coefficients R2 > 0.95. Moreover, the rate constant achieved in the EC/PDS/Cu-AC system (0.052 min−1) was higher than the sum of rate constants when AO7 was individually removed in the EC (0.017 min−1) and PDS/Cu-AC systems (0.021 min−1). It indicated that there existed a synergistic effect in terms of decolorization rate between electrochemical and the heterogeneous activation of PDS by Cu-AC (Zhang et al. 2013; Wang et al. 2014; Lin et al. 2014a).
In order to verify the contribution of copper activation, a comparative experiment was performed using fresh AC and spent AC (Cu-AC) as catalyst in the EC/heterogeneous activation process. As shown in Figure 1(d), the decolorization rate in the EC/PDS/Cu-AC system was higher than that in the EC/PDS/AC system, and the corresponding rate constant was 0.052 versus 0.034 min−1. As a result, the EC/PDS/Cu-AC process could achieve higher decolorization efficiency (95.7%) than the EC/PDS/AC process (87.1%). Considering Cu-AC exhibited nearly the same adsorption capacity as AC, it can be concluded that the spent AC was superior to the fresh one to activate PDS.
Reusability of Cu-AC catalyst
Effect of operating conditions
As depicted in Figure 3(b), initial pH (pH0) had insignificant effect on the rate constant. Despite this, the highest rate constant was obtained at pH0 5.0, which was in agreement with the largest decomposition of PDS achieved at this pH value. Unfortunately, at pH0 5.0 or even 7.0, the leached copper was higher than 0.5 mg/L, the discharge standard of China (GB 8978-1996). The leached copper decreased to below 0.5 mg/L when pH0 rose to 9.0.
With Cu-AC dosage increasing from 0.125 to 0.250 g/L, the decomposition percentage of PDS increased from 68.0 to 74.3% and, consequently, the rate constant increased from 0.036 to 0.043 min−1 (Figure 3(c)). More ≡Cu(I) would be produced through Equation (6) at higher Cu-AC dosage, and then more sulfate radicals would be generated via Equation (7). A slight increase was observed with a further increase of Cu-AC dosage.
Reaction mechanism in the EC/PDS/Cu-AC system
The variation of UV-vis spectra and TOC
Figure 5(a) illustrates that the absorption spectrum of AO7 has three main adsorption bands at 225, 310 and 485 nm. All the bands decreased as the reaction proceeded, indicating the azo bond and benzene-like structures in the AO7 molecule were destroyed (Cai et al. 2015a).
Figure 5(b) shows that although 92.4% decolorization efficiency was obtained after a 60 min reaction, only 27.3% of TOC was removed. When the time was extended to 180 min, TOC removal rose to 38.3%. To achieve high mineralization efficiency, a very high PDS to AO7 mole ratio and very long reaction time are needed (Zhou et al. 2015).
The exhausted Cu-AC was applied as catalyst in a novel EC/PDS/Cu-AC process to efficiently oxidize AO7 in aqueous solution. A radical quenching study revealed that the oxidization of AO7 occurred on the surface of Cu-AC and both SO4•– and HO• were responsible for AO7 degradation. Recycle experiments showed Cu-AC catalyst was stable and could be reused. It showed the spent AC saturated with metals such as copper could be used as an efficient catalyst in SO4•–-based AOPs, which may provide a new application of metal exhausted AC.